140CrV1
2014-09-17 10:16:09 Origin： Remark：0 Click：
Specifications 140CrV1 Datasheet, Pricelist 140CrV1 Chemical, Inventry 140CrV1 properties from Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or rough turned machining. Technical specifications - ISO 4597 - 2001. We also possess the advanced precision machining equipments for catering for your different special requirements.
DIN 140CrV1 & W-Nr 1.2206 - DATA SHEET
MATERIAL CATEGORY: Cold work alloy tool steel
TYPICAL APPLICATIONS
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / EAF + VD + LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the softened condition.
Final heat treatment - heat treatment / QT
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000 , DIN 17350 (1980)
AVAILABLE SHAPES
Round bar / flat bar / square bar / forgings
Bright - peeled + polishing /centerless grinding / peeled + slidabrading
Forged - ring /tube /pipe casing /discs /shaft
PRODUCT PROFILE AND DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 10mm to 600mm
Plate / Sheet steel / Steel strip: 0.5mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 1.35 ~ 1.45
Si (％): 0.15 ~ 0.35
Mn (％): 0.25 ~ 0.40
P (％)≤: 0.025
S (％)≤: 0.025
Cr (％): 0.20 ~ 0.40
Mo (％): —
V (％): 0.10 ~ 0.15
Si (％): 0.15 ~ 0.35
Mn (％): 0.25 ~ 0.40
P (％)≤: 0.025
S (％)≤: 0.025
Cr (％): 0.20 ~ 0.40
Mo (％): —
V (％): 0.10 ~ 0.15
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1050～850
Annealing temperature /℃: 710～740
Hardness after annealing ≤HBW: 210
Annealing temperature /℃: 710～740
Hardness after annealing ≤HBW: 210
Quenching temperature /℃: 770～740
Cooling medium: water / water
Common tempering temperature /℃: 100~150
Hardness after tempering at temperature HRC|100℃: 65
Hardness after tempering at temperature HRC|200℃: 62
Hardness after tempering at temperature HRC|300℃: 56
Hardness after tempering at temperature HRC|400℃: --
Cooling medium: water / water
Common tempering temperature /℃: 100~150
Hardness after tempering at temperature HRC|100℃: 65
Hardness after tempering at temperature HRC|200℃: 62
Hardness after tempering at temperature HRC|300℃: 56
Hardness after tempering at temperature HRC|400℃: --
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to email or call our resident team of qualified production engineers. E-mail: sales@ccsteels.com