MATERIAL DATASHEET - DIN 115CrV3
MATERIAL CATEGORY - Cold work alloy tool steel
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000 , DIN 17350 (1980)
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 1.10 ~ 1.25
Silicon, Si (％): 0.15 ~ 0.30
Manganese, Mn (％): 0.20 ~ 0.40
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 0.50 ~ 0.80
Molybdenum, Mo (％): -
Vanadium, V (％): 0.07 ~ 0.12
Silicon, Si (％): 0.15 ~ 0.30
Manganese, Mn (％): 0.20 ~ 0.40
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 0.50 ~ 0.80
Molybdenum, Mo (％): -
Vanadium, V (％): 0.07 ~ 0.12
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1050～850
Annealing temperature /℃: 710～740
Hardness after annealing ≤HBW: 220
Annealing temperature /℃: 710～740
Hardness after annealing ≤HBW: 220
Quenching temperature /℃: 760～840
Cooling medium: water / water/oil
Common tempering temperature /℃: 180~250
Hardness after tempering at temperature HRC|100℃: 64
Hardness after tempering at temperature HRC|200℃: 61
Hardness after tempering at temperature HRC|300℃: 58
Hardness after tempering at temperature HRC|400℃: --
Cooling medium: water / water/oil
Common tempering temperature /℃: 180~250
Hardness after tempering at temperature HRC|100℃: 64
Hardness after tempering at temperature HRC|200℃: 61
Hardness after tempering at temperature HRC|300℃: 58
Hardness after tempering at temperature HRC|400℃: --
TYPICAL APPLICATIONS
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutting tools, Mechanical parts, Air hammer tools, Piercing tools.
AVAILABLE SHAPES
Round bar / flat bar / square bar / plate / ring.
Bright - peeled + polishing /centerless grinding / peeled + slidabrading.
Forged - ring /tube /pipe casing /discs /shaft.
PRODUCT DESCRIPTION
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the softened condition.
Final heat treatment - heat treatment / QT
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5 to 550mm
Square bar / Flat bar: 10 to 1000mm
Plate / Sheet steel / Steel strip: 0.1mm to 200mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts / other different shapes based on OEM.