1.2210
2014-09-17 15:52:01 Origin： Remark：0 Click：
Specifications 1.2210 datasheet, 1.2210 Chemical, 1.2210 Properties from Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MATERIAL STANDARDS DATASHEET - W-Nr 1.2210
MATERIAL CATEGORY - Cold work alloy tool steel
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000, DIN 17350 (1980)
TYPICAL APPLICATIONS
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
PRODUCT DESCRIPTION
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the softened condition.
Final heat treatment - heat treatment / QT
AVAILABLE SHAPES
Black bar /Flat bar /Square bar
Bright - peeled + polishing /centerless grinding / peeled + slidabrading
Forged - ring /tube /pipe casing /discs /shaft
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 1.10 ~ 1.25
Si (％): 0.15 ~ 0.30
Mn (％): 0.20 ~ 0.40
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 0.50 ~ 0.80
Mo (％): -
V (％): 0.07 ~ 0.12
Si (％): 0.15 ~ 0.30
Mn (％): 0.20 ~ 0.40
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 0.50 ~ 0.80
Mo (％): -
V (％): 0.07 ~ 0.12
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1050～850
Annealing temperature /℃: 710～740
Hardness after annealing ≤HBW: 220
Annealing temperature /℃: 710～740
Hardness after annealing ≤HBW: 220
Quenching temperature /℃: 760～840
Cooling medium: water / water/oil
Common tempering temperature /℃: 180~250
Hardness after tempering at temperature HRC|100℃: 64
Hardness after tempering at temperature HRC|200℃: 61
Hardness after tempering at temperature HRC|300℃: 58
Hardness after tempering at temperature HRC|400℃: --
Cooling medium: water / water/oil
Common tempering temperature /℃: 180~250
Hardness after tempering at temperature HRC|100℃: 64
Hardness after tempering at temperature HRC|200℃: 61
Hardness after tempering at temperature HRC|300℃: 58
Hardness after tempering at temperature HRC|400℃: --
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 1000mm
Plate / Sheet steel / Steel strip: 0.1mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.