1.2241
2014-09-17 16:01:16 Origin： Remark：0 Click：
Specifications 1.2241 Data sheet, Stocklist 1.2241 Chemical, Inventory Suppliers 1.2241 Properties from Steelmaking, ESR melted, Blooming, Hot forging % rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or rough turned machining. Technical specifications - ISO 4597 - 2001. We also possess the advanced precision machining equipments for catering for your different special requirements.
MATERIAL DATA SHEET - Grade 1.2241
MATERIAL CATEGORY - Cold work alloy tool steel
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000, DIN 17350
MELTING PROCESS - EAF + AOD / + ESR
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
Official Test Certificate - issued by TUV - SGS - BV
CHEMICAL COMPOSITION ( Mass Weight % )
C (％): 0.47 ~ 0.55
Si (％): 0.15 ~ 0.35
Mn (％): 0.80 ~ 1.10
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 0.90 ~ 1.20
Mo (％): -
V (％): 0.10 ~ 0.20
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1000 ~ 800
Annealing temperature /℃: 700 ~ 750
Hardness after annealing ≤HBW: 220
Quenching temperature /℃: 800 ~ 830
Cooling medium: liquid
MATERIAL CATEGORY - Cold work alloy tool steel
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000, DIN 17350
MELTING PROCESS - EAF + AOD / + ESR
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
Official Test Certificate - issued by TUV - SGS - BV
CHEMICAL COMPOSITION ( Mass Weight % )
C (％): 0.47 ~ 0.55
Si (％): 0.15 ~ 0.35
Mn (％): 0.80 ~ 1.10
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 0.90 ~ 1.20
Mo (％): -
V (％): 0.10 ~ 0.20
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1000 ~ 800
Annealing temperature /℃: 700 ~ 750
Hardness after annealing ≤HBW: 220
Quenching temperature /℃: 800 ~ 830
Cooling medium: liquid
General tempering temp./℃: 180 ~ 300
Hardness after tempering at temperature HRC|100℃: 56
Hardness after tempering at temperature HRC|200℃: 54
Hardness after tempering at temperature HRC|300℃: 51
Hardness after tempering at temperature HRC|400℃: 47
Hardness after tempering at temperature HRC|200℃: 54
Hardness after tempering at temperature HRC|300℃: 51
Hardness after tempering at temperature HRC|400℃: 47
AVAILABLE SHAPES
Round bar / flat bar / plate / tube / forgings / strip / valve body
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
Round bar / flat bar / plate / tube / forgings / strip / valve body
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
FORMS AND DIMENSIONS
Round bar (Diameter): 5.5 to 650mm
Steel strip: THK0.15 ~ 2.50 X W8.0 ~ 600mm
Flat bar (Thickness X width): 10 ~ 350 X 15 ~ 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
TYPICAL APPLICATIONS
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: les@ccsteels.com
Round bar (Diameter): 5.5 to 650mm
Steel strip: THK0.15 ~ 2.50 X W8.0 ~ 600mm
Flat bar (Thickness X width): 10 ~ 350 X 15 ~ 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
TYPICAL APPLICATIONS
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: les@ccsteels.com
Hot search：1.2241
Previous page：DIN 51CrV4
Last page：59CrV4