1.2307
2014-09-17 22:11:34 Origin： Remark：0 Click：
Technical specifications of EN ISO 4957 - 2000 & DIN 17350 (1980) cold work tool steel, 1.2307 Chemical composition, 1.2307 Mechanical properties from steelmaking, hot forging, 1.2307 hot rolling, heat treatment,Straightening, 100% Ultrasonic test, Cold worked or Machined. Technical specifications - ISO 4957 - 2000.
DIN 29CrMoV9 & W-Nr 1.2307 - DATA SHEET
MATERIAL CATEGORY: Cold work alloy tool steel
TYPICAL APPLICATIONS
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
PRODUCT DESCRIPTION
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the softened condition.
Final heat treatment - heat treatment / QT
MATERIAL SPECIFICATIONS
EN ISO 4957: 2000 , DIN 17350 (1980)
AVAILABLE SHAPES
Black bar /Flat bar /Square bar
Bright - peeled + polishing /centerless grinding / peeled + slidabrading
Forged - ring /tube /pipe casing /discs /shaft
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.26 ~ 0.34
Si (％): 0.15 ~ 0.35
Mn (％): 0.40 ~ 0.70
P (％)≤: 0.035
S (％)≤: 0.035
Cr (％): 2.30 ~ 2.70
Mo (％): 0.15 ~ 0.25
V (％): 0.10 ~ 0.20
Si (％): 0.15 ~ 0.35
Mn (％): 0.40 ~ 0.70
P (％)≤: 0.035
S (％)≤: 0.035
Cr (％): 2.30 ~ 2.70
Mo (％): 0.15 ~ 0.25
V (％): 0.10 ~ 0.20
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1050～850
Annealing temperature /℃: 680～720
Hardness after annealing ≤HBW: 240
Annealing temperature /℃: 680～720
Hardness after annealing ≤HBW: 240
Quenching temperature /℃: 850～880
Cooling medium: oil
Common tempering temperature /℃: 400~600
Hardness after tempering at temperature HRC|100℃: (880～1080)MPa(+ carburization)
Hardness after tempering at temperature HRC|200℃: (880～1080)MPa(+ carburization)
Hardness after tempering at temperature HRC|300℃: (880～1080)MPa(+ carburization)
Hardness after tempering at temperature HRC|400℃: (880～1080)MPa(+ carburization)
Cooling medium: oil
Common tempering temperature /℃: 400~600
Hardness after tempering at temperature HRC|100℃: (880～1080)MPa(+ carburization)
Hardness after tempering at temperature HRC|200℃: (880～1080)MPa(+ carburization)
Hardness after tempering at temperature HRC|300℃: (880～1080)MPa(+ carburization)
Hardness after tempering at temperature HRC|400℃: (880～1080)MPa(+ carburization)
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to email or call our resident team of qualified production engineers. E-mail: sales@ccsteels.com
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 600mm
Plate / Sheet steel / Steel strip: 0.1mm to 1200mm
Width: 8mm to 2500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Hot search：1.2307
Previous page：DIN 29CrMoV9
Last page：40CrMnMo7