Specifications 1.2002 datasheet, 1.2002 Chemical, 1.2002 properties from steelmaking, hot forging, hot rolling, heat treatment, cold working. We also possess advanced precision machining equipments for further processing
MATERIAL DATA SHEET - W-Nr 1.2002
MATERIAL CATEGORY - Cold work alloy tool steel
TYPICAL APPLICATIONS
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
PRODUCT DESCRIPTION
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the softened condition.
Final heat treatment - heat treatment / QT
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000 , DIN 17350
AVAILABLE SHAPES
Round bar / flat bar / plate / tube / forge piece
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 1.20 ~ 1.30
Si (％): 0.15 ~ 0.30
Mn (％): 0.25 ~ 0.40
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 0.30 ` 0.40
Mo (％): -
V (％): -
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Si (％): 0.15 ~ 0.30
Mn (％): 0.25 ~ 0.40
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 0.30 ` 0.40
Mo (％): -
V (％): -
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1000～800
Annealing temperature /℃: 700～720
Hardness after annealing ≤HBW: 200
Quenching temperature /℃: 770～800
Cooling medium: water
Common tempering temperature /℃: 180～200
Hardness after tempering at temperature HRC|100℃: 66
Hardness after tempering at temperature HRC|200℃: 63
Hardness after tempering at temperature HRC|300℃: 57
Hardness after tempering at temperature HRC|400℃: 50
Annealing temperature /℃: 700～720
Hardness after annealing ≤HBW: 200
Quenching temperature /℃: 770～800
Cooling medium: water
Common tempering temperature /℃: 180～200
Hardness after tempering at temperature HRC|100℃: 66
Hardness after tempering at temperature HRC|200℃: 63
Hardness after tempering at temperature HRC|300℃: 57
Hardness after tempering at temperature HRC|400℃: 50
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.0mm to 500mm
Square bar / Flat bar: 3mm to 1000mm
Plate / Sheet steel / Steel strip: 0.1mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.