BF1 /1.2414
2016-01-21 12:00:06 Origin： Remark：0 Click：
Technical specifications of BS standards Cold work alloy tool steel BF1 datasheet, BF1 /1.2414 Chemical compositions, BF1 /1.2414 Mechanical properties from Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working, Peeled or rough turned machining. Technical specification - BS 4659/1989. We also possess the advanced precision machining equipments for catering for your different special requirements.
Technical Specifications Data Sheet: BF1 /1.2414
OFFICIAL TEST REPORT: issued by TUV - SGS - BV
MATERIAL CATEGORY: Cold work alloy tool steel
MATERIAL SPECIFICATIONS: BS 4659 - 89
CHEMICAL COMPOSITION (WEIGHT - %)
C (％): 1.15~1.35
Si (％): ≤0.40
Mn (％): ≤0.40
P (％)≤: 0.030
S (％)≤: 0.030
Mn (％): ≤0.40
P (％)≤: 0.030
S (％)≤: 0.030
Cr (%): 0.25~0.50
Mo (％): -
W (%): 1.30~1.60
V (%): ≤0.30
HEAT TREATMENT PRACTICE AND HARDNESS
Annealing temperature ℃: 780~800
Hardness after annealing ≤HBW: 207
Preheating temperature ℃ /: -
Annealing temperature ℃: 780~800
Hardness after annealing ≤HBW: 207
Preheating temperature ℃ /: -
Quenching temperature ℃: 780~800
Cooling medium: oil / water cooled
Cooling medium: oil / water cooled
Tempering temperature ℃: 200~250
Hardness value after tempered /≥ HV: 760
MELTING PROCESS
This alloy is generally smelt in electric arc furnace (EAF ) or IFF + VD, LF + Electroslag remelting (ESR).
Hardness value after tempered /≥ HV: 760
MELTING PROCESS
This alloy is generally smelt in electric arc furnace (EAF ) or IFF + VD, LF + Electroslag remelting (ESR).
For a purpose of higher quality, it should be smelt via technology of vacuum refining.
TYPICAL APPLICATIONS
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutlery for medical equipments
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutlery for medical equipments
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
Mechanical parts
Air hammer tools
Piercing tools
HEAT TREATTMENT PRACTICE
The preheating of measuring and cutting tool steel is spheroidizing annealing, final heat treatment is quenching + low temperature tempering and hardness after heat treatment can reach 60~65HRC. When heat treat tool steel grades consideration should be given to hardening temperature, including ratio of heating, cooling and soaking times which will differ due to factors such as the shape and size of each chemical component. Other considerations during heat treatment include the type of furnace, quenching medium and work piece transfer facilities.
The preheating of measuring and cutting tool steel is spheroidizing annealing, final heat treatment is quenching + low temperature tempering and hardness after heat treatment can reach 60~65HRC. When heat treat tool steel grades consideration should be given to hardening temperature, including ratio of heating, cooling and soaking times which will differ due to factors such as the shape and size of each chemical component. Other considerations during heat treatment include the type of furnace, quenching medium and work piece transfer facilities.
FEATURES AND CLASSIFICATIONS
Hot-work die divides into several main types, such as hammer forging, die forging, extrusion and die casting, including hot forging die, press machine forging die, stamping die, hot-extrusion die, metal die-casting mould. Heat distortion mould not only supports huge mechanical stress, but also thermal stress during working repeatedly. Hot-work die steel should have not only high hardness, red hardness, abrasion resistance, toughness, but also have excellent high temperature strength, thermal fatigue stability, thermal conductivity, upper hardenability for guaranteeing the whole cross section with consistent mechanical property.
Hot-work die divides into several main types, such as hammer forging, die forging, extrusion and die casting, including hot forging die, press machine forging die, stamping die, hot-extrusion die, metal die-casting mould. Heat distortion mould not only supports huge mechanical stress, but also thermal stress during working repeatedly. Hot-work die steel should have not only high hardness, red hardness, abrasion resistance, toughness, but also have excellent high temperature strength, thermal fatigue stability, thermal conductivity, upper hardenability for guaranteeing the whole cross section with consistent mechanical property.
PRODUCT PROFILE
Round bar (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar (Diameter): 0.50mm to 800mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Steel strip: T0.20 ~ 3mm X W10 ~ 2000mm X Coil
Heavy/middle plate via hot rolled: T4 - 200mm X W1000- 2500mm X L1000-12000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Heavy/middle plate via hot rolled: T4 - 200mm X W1000- 2500mm X L1000-12000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
- Email us: lh.steel@hotmail.com
Previous page：B62
Last page：BL1 / 1.2067