ISO X40Cr14
2016-03-08 08:47:51 Origin： Remark：0 Click：
X40Cr14 Global Wholesalers Die Steel, X40Cr14 Tool Die steel Suppliers & Manufacturers,X40Cr14 Forging Bar plate machined, X40Cr14 Tool Steel exporters. Technical Specifications - EN ISO 4957: 2000. From Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic flaw detection test.
TECHNICAL DATA SHEET: ISO X40Cr14
OFFICIAL TEST REPORT: issued by TUV - SGS - BV
MATERIAL CATEGORY: cold work alloy tool steel
MATERIAL SPECIFICATIONS: ISO 4957 - 1999
CHEMICAL COMPOSITION (WEIGHT - %)
C (％): 0.36 ~ 0.42
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.030
S (％)≤: 0.030
Cr (%): 12.5 ~ 14.5
Mo (％): -
V (%): -
P (％)≤: 0.030
S (％)≤: 0.030
Cr (%): 12.5 ~ 14.5
Mo (％): -
V (%): -
HEAT TREATMENT AND HARDNESS FOR COLD WORK ALLOY TOOL STEEL
Hardness after annealing ≤HBW : 241
Quenching temperature ℃ ±10℃ : 1010
Hardness after annealing ≤HBW : 241
Quenching temperature ℃ ±10℃ : 1010
Cooling medium: Oil
Tempering temperature ℃ ±10℃ : 180
Hardness value after tempering /≥ HRC: 300HBW (hardened condition)
MELTING PROCESS
This alloy is generally smelt in electric arc furnace (EAF ) or IFF + VD, LF + Electroslag remelting (ESR).
For a purpose of higher quality, it should be smelt via technology of vacuum refining.
TYPICAL APPLICATIONS
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutlery for medical equipments
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
HEAT TREATTMENT PRACTICE
The preheating of measuring and cutting tool steel is spheroidizing annealing, final heat treatment is quenching + low temperature tempering and hardness after heat treatment can reach 60~65HRC. When heat treat tool steel grades consideration should be given to hardening temperature, including ratio of heating, cooling and soaking times which will differ due to factors such as the shape and size of each chemical component. Other considerations during heat treatment include the type of furnace, quenching medium and work piece transfer facilities.
FEATURES AND CLASSIFICATIONS
Hot-work die divides into several main types, such as hammer forging, die forging, extrusion and die casting, including hot forging die, press machine forging die, stamping die, hot-extrusion die, metal die-casting mould. Heat distortion mould not only supports huge mechanical stress, but also thermal stress during working repeatedly. Hot-work die steel should have not only high hardness, red hardness, abrasion resistance, toughness, but also have excellent high temperature strength, thermal fatigue stability, thermal conductivity, upper hardenability for guaranteeing the whole cross section with consistent mechanical property.
PRODUCT PROFILE AND AVAILABLE FORMS
Round bar (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Length: random length, fixed length or based on the customer's special requirement.
Steel strip: T0.50 ~ 3mm X W10 ~ 1000mm X Coil
Heavy/middle plate via hot rolled: T60 - 300mm X W100 - 1200mm X L1000 ~ 4000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
This alloy is generally smelt in electric arc furnace (EAF ) or IFF + VD, LF + Electroslag remelting (ESR).
For a purpose of higher quality, it should be smelt via technology of vacuum refining.
TYPICAL APPLICATIONS
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutlery for medical equipments
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
HEAT TREATTMENT PRACTICE
The preheating of measuring and cutting tool steel is spheroidizing annealing, final heat treatment is quenching + low temperature tempering and hardness after heat treatment can reach 60~65HRC. When heat treat tool steel grades consideration should be given to hardening temperature, including ratio of heating, cooling and soaking times which will differ due to factors such as the shape and size of each chemical component. Other considerations during heat treatment include the type of furnace, quenching medium and work piece transfer facilities.
FEATURES AND CLASSIFICATIONS
Hot-work die divides into several main types, such as hammer forging, die forging, extrusion and die casting, including hot forging die, press machine forging die, stamping die, hot-extrusion die, metal die-casting mould. Heat distortion mould not only supports huge mechanical stress, but also thermal stress during working repeatedly. Hot-work die steel should have not only high hardness, red hardness, abrasion resistance, toughness, but also have excellent high temperature strength, thermal fatigue stability, thermal conductivity, upper hardenability for guaranteeing the whole cross section with consistent mechanical property.
PRODUCT PROFILE AND AVAILABLE FORMS
Round bar (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 10mm to 800mm
Length: random length, fixed length or based on the customer's special requirement.
Steel strip: T0.50 ~ 3mm X W10 ~ 1000mm X Coil
Heavy/middle plate via hot rolled: T60 - 300mm X W100 - 1200mm X L1000 ~ 4000mm
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.