TECHNICAL DATA SHEET: W-Nr. 1.3392
MATERIAL CATEGORY: high speed tool steel
MATERIAL SPECIFICATIONS: DIN EN ISO 4957 - 2001
OFFICIAL TEST REPORT: issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): 0.75 ~ 0.85
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): ≤ 0.40
Phosphorus, P (％)≤: 0.030
Sulfur, S (％)≤: 0.030
Chromium, Cr (％): 4.10 ~ 5.00
Molybdenum, Mo (％): 4.50 ~ 5.20
Tungsten, W (％): 0.50 ~ 1.10
Vanadium, V (％): 1.60 ~ 2.20
Cobalt, Co (％): -
HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working temperature: 1100 ~ 900
Annealing temperature: 820 ~ 860
Annealed hardness, HBW: 270
Quenching temperature /℃, cooling medium = oil / 550℃ heating bath, air cooling
Heating temperature /℃: 450 ~ 600
First time preheat temperature /℃: 850
Second time preheat temperature /℃: 1050
Last time preheat temperature /℃: 1160 ~ 1200
Tempering temperature /℃: 530 ~ 560
Hardness after tempering ≥HRC: 63
APPLICATION FIELD
High speed steel is generally widely used in the field of machining at high speeds. With the excellent abrasion resistance, high temperature properties and excellent hardness, high speed steels (HSS) have become material a wide range of applications including cutting tools, such as drills, taps, milling cutters, tool bits, gear cutters, saw blades and rolls, such as hot strip mill finishing train, rod and bar mill finishing, universal mill finishing. High speed steels also found a market in fine hand tools where their relatively fine toughness at high hardness, coupled with high abrasion resistance, made them suitable for low speed applications requiring a durable edge, such as chisels, hand plane, blades, and high quality kitchen hardware, pocket knives, swords.
MELTING PROCESS
This alloy is generally smelt in electric arc furnace (EAF ), EF or IFF + VD, LF + Electroslag remelting (ESR).
For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
PRODUCT PROFILE AND DIMENSIONS
Round bar (diameter): 5.5 mm to 300mm
Square bar / Flat bar: 10mm to 500mm
Wire rod (diameter): 0.10 ~ 15mm
Length: random length, fixed length or based on the customer's special requirement.
Steel strip: T0.10 ~ 3mm X W10 ~ 1200mm X Coil
Heavy/middle plate via hot rolled: T4 - 200mm X W1000- 1500mm X L1000-12000mm
Forging piece: stepped shafts, other different shapes based on OEM.
Cobalt, Co (％): -
HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working temperature: 1100 ~ 900
Annealing temperature: 820 ~ 860
Annealed hardness, HBW: 270
Quenching temperature /℃, cooling medium = oil / 550℃ heating bath, air cooling
Heating temperature /℃: 450 ~ 600
First time preheat temperature /℃: 850
Second time preheat temperature /℃: 1050
Last time preheat temperature /℃: 1160 ~ 1200
Tempering temperature /℃: 530 ~ 560
Hardness after tempering ≥HRC: 63
APPLICATION FIELD
High speed steel is generally widely used in the field of machining at high speeds. With the excellent abrasion resistance, high temperature properties and excellent hardness, high speed steels (HSS) have become material a wide range of applications including cutting tools, such as drills, taps, milling cutters, tool bits, gear cutters, saw blades and rolls, such as hot strip mill finishing train, rod and bar mill finishing, universal mill finishing. High speed steels also found a market in fine hand tools where their relatively fine toughness at high hardness, coupled with high abrasion resistance, made them suitable for low speed applications requiring a durable edge, such as chisels, hand plane, blades, and high quality kitchen hardware, pocket knives, swords.
MELTING PROCESS
This alloy is generally smelt in electric arc furnace (EAF ), EF or IFF + VD, LF + Electroslag remelting (ESR).
For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
PRODUCT PROFILE AND DIMENSIONS
Round bar (diameter): 5.5 mm to 300mm
Square bar / Flat bar: 10mm to 500mm
Wire rod (diameter): 0.10 ~ 15mm
Length: random length, fixed length or based on the customer's special requirement.
Steel strip: T0.10 ~ 3mm X W10 ~ 1200mm X Coil
Heavy/middle plate via hot rolled: T4 - 200mm X W1000- 1500mm X L1000-12000mm
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com.
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com.
Hot search：1.3392
Previous page：JIS G4309 SUS304J3
Last page：13-8Mo / XM-13