Material standard specification of AIR 9160/C type 100C6 data sheet,9160C Grade 100C6 Chemical compositions, AIR 9160C 100C6 Mechanical properties from Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3. Cold working, Polishing, Centerless grinding, Peeling or rough turned machining. Material technical specification AIR 9160/C - 1973.
TECHNICAL SPECIFICATION - AIR 9160C Grade 100C6
TECHNICAL SPECIFICATION: DGA - AIR 9160/C - 1973
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS
MATERIAL TYPE: super high tensile steel
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.95 ~ 1.10
Si (％): 0.15 ~ 0.35
Mn (％): 0.20 ~ 0.40
P (％) ≤: 0.030
S (％) ≤: 0.020
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.95 ~ 1.10
Si (％): 0.15 ~ 0.35
Mn (％): 0.20 ~ 0.40
P (％) ≤: 0.030
S (％) ≤: 0.020
Cr (%): 1.35 ~ 1.60
Ni (%): ≤ 0.40
Mo (%): ≤ 0.10
V (%): ≤ 0.30
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Tensile strength,σb/≥ MPa: -
Yield strength, σ0.2/≥ MPa: -
Elongation, δ ≥(％): -
Reduction of area, ф ≥ (％): -
Impact, AK (J/cm2): -
Annealed / Heat treated hardness | HB: 60HRC min.
Tensile strength,σb/≥ MPa: -
Yield strength, σ0.2/≥ MPa: -
Elongation, δ ≥(％): -
Reduction of area, ф ≥ (％): -
Impact, AK (J/cm2): -
Annealed / Heat treated hardness | HB: 60HRC min.
Quenching/Solution treated, 930,+/-10 Deg, tempering 180, +/-5 Deg.
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 1.5 mm to 500mm
Square bar / Flat bar: 3mm to 500mm
Steel strip: T0.20 ~ 3mm X W10 ~ 2000mm X Coil
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 1.5 mm to 500mm
Square bar / Flat bar: 3mm to 500mm
Steel strip: T0.20 ~ 3mm X W10 ~ 2000mm X Coil
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
- Email: lh.steel@hotmail.com
Previous page：JIS G4309 SUS403
Last page：JIS G4309 SUS410