Material standard specification of AIR 9160/C type data sheet, Chemical compositions, Mechanical properties from Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3. Cold working, Polishing, Centerless grinding, Peeling or rough turned machining. Material technical specification AIR 9160/C - 1973.
TECHNICAL SPECIFICATION - AIR 9160C Grade E-Z85WCDV6
TECHNICAL SPECIFICATION: DGA - AIR 9160/C - 1973
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS
MATERIAL TYPE: super high tensile steel
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.75 ~ 0.85
Si (％): 0.10 ~ 0.40
Mn (％): 0.10 ~ 0.40
P (％) ≤: 0.030
S (％) ≤: 0.015
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.75 ~ 0.85
Si (％): 0.10 ~ 0.40
Mn (％): 0.10 ~ 0.40
P (％) ≤: 0.030
S (％) ≤: 0.015
Cr (%): 4.00 ~ 5.00
W (%): 5.50 ~ 6.50
Mo (%): 4.50 ~ 5.50
V (%): 1.50 ~ 2.00
Ni (%): ≤ 0.20
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Tensile strength,σb/≥ MPa: -
Yield strength, σ0.2/≥ MPa: -
Elongation, δ ≥(％): -
Reduction of area, ф ≥ (％): -
Impact, AK (J/cm2): -
Annealed / Heat treated hardness | HB: 60HRC min.
Tensile strength,σb/≥ MPa: -
Yield strength, σ0.2/≥ MPa: -
Elongation, δ ≥(％): -
Reduction of area, ф ≥ (％): -
Impact, AK (J/cm2): -
Annealed / Heat treated hardness | HB: 60HRC min.
Quenching/Solution treated, 820,+/-10 Deg, tempering 550, +/-5 Deg.
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 1.5 mm to 500mm
Square bar / Flat bar: 3mm to 500mm
Steel strip: T0.20 ~ 3mm X W10 ~ 2000mm X Coil
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 1.5 mm to 500mm
Square bar / Flat bar: 3mm to 500mm
Steel strip: T0.20 ~ 3mm X W10 ~ 2000mm X Coil
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
- Email: lh.steel@hotmail.com
Hot search：E-Z85WCDV6
Previous page：A535 Grade 8620
Last page：AIR9160C Z100CD17