Material technical specifications of NF A35 - 590-1992 high speed tool steel HS18-0-1 data sheet, HS18-0-1 Chemical compositions, HS18-0-1 Mechanical properties from Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling,HS18-0-1 Heat treatment, Straightening, 100% Ultrasonic test, Cold working, Peeled or rough turned machining. Technical specification - NF A35 - 590 1992. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET: NF HS18-0-1
MATERIAL CATEGORY: High speed tool steel
MATERIAL SPECIFICATIONS: NF A35 - 590-1992
OFFICIAL TEST REPORT: issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): 0.72 ~ 0.80
Si (％): ≤ 0.50
Mn (％): ≤ 0.40
P (％)≤: 0.030
S (％)≤: 0.030
Co (%): -
Cr (%): 3.50 ~ 4.50
Mo (%): -
V (%): 1.00 ~ 1.30
W (%): 17.2 ~ 18.7
MECHANICAL PROPERTY AND HARDNESS
Annealed hardness, ≤ HB: 270
Annealed hardness, ≤ HB: 270
Quenching temperature /℃: 1240, salt bath
Tempering temperature /℃: 550 X 2
Hardness in quenched condition, HRC: 63 min.
MELTING PROCESS
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, LF + Electroslag remelting (ESR).
For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
PRODUCT PROFILE AND AVAILABLE FORMS
Round bar (Diameter): 6mm to 2000mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
MELTING PROCESS
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, LF + Electroslag remelting (ESR).
For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
PRODUCT PROFILE AND AVAILABLE FORMS
Round bar (Diameter): 6mm to 2000mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
- Email us: lh.steel@hotmail.com
Previous page：NF HS6-5-4-2
Last page：B649 Gr.R20033