DIN X63CrMoV5-1
2014-10-01 21:02:42 Origin： Remark：0 Click：
※DINX63CrMoV5-1/ W-Nr 1.2362 - DATA SHEET ※※ MATERIALCATEGORY: Cold work alloytool steel※ TYPICAL APPLICATIONSAll...
※ DIN X63CrMoV5-1 / W-Nr 1.2362 - DATA SHEET ※
※ MATERIAL CATEGORY: Cold work alloy tool steel
※ TYPICAL APPLICATIONS
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
※ PRODUCT DESCRIPTION
The alloy is usually produced by EAF /VD /LF /IFF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the
buyers' requirements.
Bars are usually supplied bright (peeling or centreless grinding) in the softened condition.
Final heat treatment - heat treatment / QT
※ MATERIAL SPECIFICATIONS
EN ISO 4957: 2000 , DIN 17350 (1980)
※ AVAILABLE SHAPES
Black bar /Flat bar /Square bar
Bright - peeled + polishing /centerless grinding / peeled + slidabrading
Forged - ring /tube /pipe casing /discs /shaft
※ CHEMICAL COMPOSITION (WEIGHT %) - DIN X63CrMoV5-1 / W-Nr 1.2362
C(％): 0.60～0.65
Si(％): 1.00～1.20
Mn(％): 0.30～0.50
P(％)≤: 0.035
S(％)≤: 0.035
Cr(％): 5.00～5.50
Mo(％): 1.00～1.30
V(％): 0.25～0.35
Si(％): 1.00～1.20
Mn(％): 0.30～0.50
P(％)≤: 0.035
S(％)≤: 0.035
Cr(％): 5.00～5.50
Mo(％): 1.00～1.30
V(％): 0.25～0.35
Other(%): -
※ MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1000～800
Annealing temperature /℃: 800～820
Hardness after annealing ≤HBW: 225
Annealing temperature /℃: 800～820
Hardness after annealing ≤HBW: 225
Quenching temperature /℃: 980~1000
Cooling medium: oil or air cooling
Cooling medium: oil or air cooling
Common tempering temperature /℃: 400~550
Hardness after tempering at temperature /MPa |400℃: 57HRC
Hardness after tempering at temperature /MPa |400℃: 57HRC
Hardness after tempering at temperature /MPa |500℃: 57HRC
Hardness after tempering at temperature /MPa |600℃: 48HRC
Hardness after tempering at temperature /MPa |650℃: -
Hardness after tempering at temperature /MPa |650℃: -
※ INVENTORY - hot rolled bar
Diameter: 20mm
Quantity: 48kg
Diameter: 20mm
Quantity: 48kg
※ TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
Round bar / Wire rod (Diameter): 0.50mm to 3000mm
Square bar / Flat bar: 3mm to 2000mm
Plate / Sheet steel / Steel strip: 0.1mm to 2500mm
Width: 8mm to 2500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.
Hot search：DIN X63CrMoV5-1