1.2362
2014-10-01 21:09:57 Origin： Remark：0 Click：
Specifications 1.2362 Datasheet, Inventory X63CrMoV5-1 Chemical, Stocklist 1.2362 Properties from steelmaking, Hot forging, hot rolling, Heat treatment
MATERIAL DATA SHEET - W-Nr 1.2362
MATERIAL CATEGORY - Hot work alloy tool steel
TYPICAL APPLICATIONS
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
PRODUCT DESCRIPTION
The alloy is usually produced by EAF /VD /LF /IFF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the
buyers' requirements.
Bars are usually supplied bright (peeling or centreless grinding) in the softened condition.
Final heat treatment - heat treatment / QT
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000 , DIN 17350 (1980)
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 1100mm
Plate / Sheet steel / Steel strip: 0.1mm to 1000mm
Width: 8mm to 1200mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
CHEMICAL COMPOSITION ( mass weight - % )
Carbon, C (％): 0.60 ~ 0.65
Silicon, Si (％): 1.00 ~ 1.20
Manganese, Mn (％): 0.30 ~ 0.50
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.035
Chromium, Cr (％): 5.00 ~ 5.50
Molybdneum, Mo (％): 1.00 ~ 1.30
Vanadium, V (％): 0.25 ~ 0.35
Silicon, Si (％): 1.00 ~ 1.20
Manganese, Mn (％): 0.30 ~ 0.50
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.035
Chromium, Cr (％): 5.00 ~ 5.50
Molybdneum, Mo (％): 1.00 ~ 1.30
Vanadium, V (％): 0.25 ~ 0.35
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1000～800
Annealing temperature /℃: 800～820
Hardness after annealing ≤HBW: 225
Annealing temperature /℃: 800～820
Hardness after annealing ≤HBW: 225
Quenching temperature /℃: 980~1000
Cooling medium: oil or air cooling
Cooling medium: oil or air cooling
Common tempering temperature /℃: 400~550
Hardness after tempering at temperature /MPa |400℃: 57HRC
Hardness after tempering at temperature /MPa |400℃: 57HRC
Hardness after tempering at temperature /MPa |500℃: 57HRC
Hardness after tempering at temperature /MPa |600℃: 48HRC
Hardness after tempering at temperature /MPa |650℃: -
Hardness after tempering at temperature /MPa |650℃: -
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com