T13143
2017-10-09 15:10:55   Origin:   Remark:0 Click:

Material Technical Standard of ASTM A600 - 2004 high speed tool steel T13143 datasheet, UNS T13143 Chemical composition,UNS T13143 Mechanical property from Steelmaking,ESR melted,Hot blooming, T13143 Hot forging, Hot rolling, Heat treatment, Straightening,100% Ultrasonic flaw test, Cold working, Peeled or rough turned machining.Technical specification - ASTM A600 - 2004. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MATERIAL TECHNICAL DATA SHEET:  UNS T13143

MATERIAL CATEGORY: Mo - W series High speed tool steel
MATERIAL SPECIFICATIONS: ASTM A600 - 2004
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (%):     1.15 ~ 1.25
Si (%):     0.15 ~ 0.65
Mn (%):   0.20 ~ 0.40
P (%)≤:   0.030

S (%)≤:   0.030
Cr (%):    3.50 ~ 4.25
Mo (%):   7.50 ~ 8.50
W (%):    2.25 ~ 3.00
V (%):     1.50 ~ 1.75
Co (%):   7.75 ~ 8.75 
HEAT TREATMENT PRACTICE AND HARDNESS
Annealing temperature /℃: 880 ~ 900
Annealed hardness, ≤ HB: 269
Quenching temperature /℃: 1160 ~ 1180
Cooling medium: oil, air
Tempering temperature /℃: 530 ~ 550
Hardness under tempered condition ≥HRC: 66
MELTING PROCESS
This
alloy is generally smelt in Non-vacuum furnace + ESR, Electric Arc Furnace  (EAF), EAF+LF+VD, LF + ESR.
For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.

TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
- Email us:
lh.steel@hotmail.com 

Hot search:T13143

Previous page:AISI M43 / ASTM M43
Last page:T13142

Share to: