T13142
2017-10-09 15:13:36 Origin： Remark：0 Click：
Material Technical Standard of ASTM A600 - 2004 high speed tool steel T13142 data sheet,UNS T13142 Chemical composition,UNS T13142 Mechanical property from Steelmaking, ESR melted, Hot blooming, M42 Hot forging, Hot rolling,Heat treatment, Straightening, 100% Ultrasonic flaw test, Cold working, Peeled or rough turned machining. Technical specification - ASTM A600 - 2004. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MATERIAL TECHNICAL DATA SHEET: T13142
MATERIAL CATEGORY: Mo - W series High speed tool steel
MATERIAL SPECIFICATIONS: ASTM A600 - 2004
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): 1.05 ~ 1.15
C (％): 1.05 ~ 1.15
Si (％): 0.15 ~ 0.65
Mn (％): 0.15 ~ 0.40
P (％)≤: 0.030
S (％)≤: 0.030
Mn (％): 0.15 ~ 0.40
P (％)≤: 0.030
S (％)≤: 0.030
Cr (%): 3.50 ~ 4.25
Mo (%): 9.00 ~ 10.0
W (%): 1.15 ~ 1.85
V (%): 0.95 ~ 1.35
Co (%): 7.75 ~ 8.75
HEAT TREATMENT PRACTICE AND HARDNESS
Annealing temperature /℃: 770 ~ 820
Annealed hardness, ≤ HB: 240 ~ 300
Quenching temperature /℃: 1170 ~ 1210
Cooling medium: oil, air
Tempering temperature /℃: 530 ~ 550
Hardness under tempered condition ≥HRC: 69 ~ 66
Tempering temperature /℃: 530 ~ 550
Hardness under tempered condition ≥HRC: 69 ~ 66
MELTING PROCESS
This alloy is generally smelt in Non-vacuum furnace + ESR, Electric Arc Furnace (EAF), EAF+LF+VD, LF + ESR.
For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
This alloy is generally smelt in Non-vacuum furnace + ESR, Electric Arc Furnace (EAF), EAF+LF+VD, LF + ESR.
For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
- Email us: lh.steel@hotmail.com
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
- Email us: lh.steel@hotmail.com
Hot search：T13142
Previous page：T13143
Last page：Z3CNDU22-07Az