T11352
2017-10-26 09:29:03   Origin:   Remark:0 Click:

Material Standard of ASTM A600 high Speed Tool Steel T11352 Round bar, Flat bar, Plate, Steelmaking, ESR melted, Heat treatment
 
TECHNICAL DATA SHEET - UNS T11352

MATERIAL CATEGORY: Mo - W series High speed tool steel
MATERIAL SPECIFICATIONS: ASTM A600 - 2004
CHEMICAL COMPOSITIONS (mass fraction - %)
Carbon, C (%): 0.85 ~ 0.95
Silicon, Si (%): 0.20 ~ 0.60
Manganese, Mn (%): 0.15 ~ 0.35
Phosphorus, P (%) ≤: 0.030

Sulfur, S (%) ≤: 0.05 ~ 0.09
Chromium, Cr (%): 3.75 ~ 4.50
Molybdenum, Mo (%): 4.15 ~ 4.75
Tungsten, W (%): 0.75 ~ 1.50
Vanadium, V (%): 1.75 ~ 2.10 
HEAT TREATMENT PRACTICE AND HARDNESS
Annealing temperature /℃: 830 ~ 850
Annealed hardness, ≤ HB: 248
Quenching temperature /℃: 1140 ~ 1160
Cooling medium: oil
Tempering temperature /℃: 520 ~ 550
Hardness under tempered condition ≥HRC: 63 ~ 61
MELTING PROCESS
This alloy
is generally smelt in Non-vacuum furnace + ESR, Electric Arc Furnace  (EAF), EAF+LF+VD, LF + ESR.
For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.

PRODUCT PROFILE AND DIMENSION
Round bar (Diameter): 5.50 to 450mm
Square bar / Flat bar: T3 to 500mm X W3 ~ 1200mm
Wire rod (Diameter):  0.30 to 13mm
Steel strip: THK0.15 ~ 2.50 X W8.0 ~ 185mm
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.

Hot search:T11352

Previous page:AISI M52 / ASTM M52
Last page:Esshete 1250

Share to: