AISI M62 / SAE M62
2025-04-15 11:10:00 Origin： Remark：0 Click：
ASTM A600-2004 high speed tool steel AISI M62 & SAE M62 Round bar, Flat bar, Plate, properties from Steelmaking, ESR melted, Hot blooming/forging/rolling, Heat treatment
TECHNICAL DATA SHEET: AISI M62 & SAE M62
CHEMICAL COMPOSITIONS (mass weight %)
Carbon, C (％): 1.75 ~ 1.85
Carbon, C (％): 1.75 ~ 1.85
Silicon, Si (％): 0.20 ~ 0.45
Manganese, Mn (％): 0.15 ~ 0.45
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.030
Manganese, Mn (％): 0.15 ~ 0.45
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.030
Chromium, Cr (%): 3.50 ~ 4.00
Molybdenum, Mo (%): 10.0 ~ 11.0
Tungsten, W (%): 5.75 ~ 6.50
Vanadium, V (%): 1.80 ~ 2.10
HEAT TREATMENT PRACTICE AND HARDNESS
Annealing temperature /℃: -
Annealed hardness, ≤ HB: 285
Quenching temperature /℃: 1190
Cooling medium: oil
Tempering temperature /℃: 540
Hardness under tempered condition HRC: 66
Tempering temperature /℃: 540
Hardness under tempered condition HRC: 66
MELTING PROCESS
This alloy is generally smelt in Non-vacuum furnace + ESR, Electric Arc Furnace (EAF), EAF+LF+VD, LF + ESR. For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
PRODUCT PROFILE AND AVAILABLE FORMS
Round bar (Diameter): 0.50 to 450mm
Square bar / Flat bar: T3 to 500mm X W3 ~ 1200mm
This alloy is generally smelt in Non-vacuum furnace + ESR, Electric Arc Furnace (EAF), EAF+LF+VD, LF + ESR. For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
PRODUCT PROFILE AND AVAILABLE FORMS
Round bar (Diameter): 0.50 to 450mm
Square bar / Flat bar: T3 to 500mm X W3 ~ 1200mm
Wire rod (Diameter): 0.30 to 13mm
Steel strip: THK0.15 ~ 2.50 X W8.0 ~ 185mm
Length: Fixed length or random length or based on the customer's special requirement.
Steel strip: THK0.15 ~ 2.50 X W8.0 ~ 185mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.