EN 28
2020-10-20 08:13:03 Origin： Remark：0 Click：
BS970 Part 3 type EN 28 Round bar, flat bar, Forgings EN 28 Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or machined.
TECHNICAL DATA SHEET - Grade EN 28
MELTING: Consumable electrode remelted
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): 0.25 ~ 0.40
Manganese, Mn (％): 0.50 ~ 0.90
Silicon, Si (％): 0.10 ~ 0.35
Phosphorus, P (％)≤: 0.035
Sulfur, S (％)≤: 0.015
Chromium, Cr (%): 0.75 ~ 1.50
Nickel, Ni (%): 3.00 ~ 4.50
Molybdenum, Mo (%): 0.20 ~ 0.65
MECHANICAL PROPERTY AND HARDNESS
Quenching temperature /℃: 860, oil
Tempering temperature /℃: 600, water or oil
Tensile strength,σb/≥ MPa: 980
Carbon, C (％): 0.25 ~ 0.40
Manganese, Mn (％): 0.50 ~ 0.90
Silicon, Si (％): 0.10 ~ 0.35
Phosphorus, P (％)≤: 0.035
Sulfur, S (％)≤: 0.015
Chromium, Cr (%): 0.75 ~ 1.50
Nickel, Ni (%): 3.00 ~ 4.50
Molybdenum, Mo (%): 0.20 ~ 0.65
MECHANICAL PROPERTY AND HARDNESS
Quenching temperature /℃: 860, oil
Tempering temperature /℃: 600, water or oil
Tensile strength,σb/≥ MPa: 980
Yield strength, σ0.2/≥ MPa: 835
Elongation, δ ≥(％): 12.0
Reduction of area, ф ≥(％): 55.0
Hardness in annealed condition: HB269 max.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
FORMS & DIMENSIONS
Round bar: 5.5mm to 550mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Elongation, δ ≥(％): 12.0
Reduction of area, ф ≥(％): 55.0
Hardness in annealed condition: HB269 max.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
FORMS & DIMENSIONS
Round bar: 5.5mm to 550mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.