EN 36A
2021-01-06 09:05:07 Origin： Remark：0 Click：
Description EN 36A datasheet, EN 36A Chemical, EN 36A Properties from Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - Grade EN 36A
MELTING: Consumable electrode remelted steel
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
OFFICIAL TEST REPORT - issued by TUV - SGS - BV
CHEMICAL COMPOSITIONS (WEIGHT - %)
C (％): 0.10 ~ 0.16
Mn (％): 0.30 ~ 0.60
Si (％): 0.10 ~ 0.35
P (％)≤: 0.025
S (％)≤: 0.015
Cr (%): 0.70 ~ 1.00
Ni (%): 3.00 ~ 3.75
Mo (%): -
MECHANICAL PROPERTY AND HARDNESS
Quenching temperature /℃:-
Tempering temperature /℃:-
Tensile strength,σb/≥ MPa: 930
C (％): 0.10 ~ 0.16
Mn (％): 0.30 ~ 0.60
Si (％): 0.10 ~ 0.35
P (％)≤: 0.025
S (％)≤: 0.015
Cr (%): 0.70 ~ 1.00
Ni (%): 3.00 ~ 3.75
Mo (%): -
MECHANICAL PROPERTY AND HARDNESS
Quenching temperature /℃:-
Tempering temperature /℃:-
Tensile strength,σb/≥ MPa: 930
Yield strength, σ0.2/≥ MPa: 730
Elongation, δ ≥(％): 15.0
Reduction of area, ф ≥(％): -
Hardness in condition of annealing +A: HB241 max.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
FORMS & AVAILABLE DIMENSIONS
Round bar: 5.5mm to 550mm
Square bar / Flat bar: 10mm to 610mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Reduction of area, ф ≥(％): -
Hardness in condition of annealing +A: HB241 max.
MELTING PROCESS & APPLICATION
This alloy is generally smelt in Electric Arc Furnace (EAF), EAF+LF+VD, BEF + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
It is suitable for applications such as high tensile shafts, bolts and nuts, gears, pinions spindles and so on.
FORMS & AVAILABLE DIMENSIONS
Round bar: 5.5mm to 550mm
Square bar / Flat bar: 10mm to 610mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.