E35NCD16H
2021-07-12 09:50:06 Origin： Remark：0 Click：
Inventory E35NCD16H Specifications, Suppliers E35NCD16H Data sheet, Chemical E35NCD16H Stockholder from Steelmelting (ESR refined), Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
MATERIAL SPECIFICATIONS DATASHEET - Grade E35NCD16H
Material Category - Aerospace Material Steel Series
Techncial Specifications - DGA - AIR 9160/C
Techncial Specifications - DGA - AIR 9160/C
Melting process - VAC + VAR / ESR
HS Code for Customs - 72283000 / 72284000 / 72285000
HS Code for Customs - 72283000 / 72284000 / 72285000
Official Test Report - issued by TUV - SGS - BV
Chemical compositions (Mass Weight %)
Chemical compositions (Mass Weight %)
C (％): 0.35 ~ 0.40
Si (％): ≤ 0.45
Mn (％): ≤ 0.60
P (％) ≤: 0.015
S (％) ≤: 0.010
Cr (％): 1.60 ~ 2.00
Si (％): ≤ 0.45
Mn (％): ≤ 0.60
P (％) ≤: 0.015
S (％) ≤: 0.010
Cr (％): 1.60 ~ 2.00
Ni (%): 3.50 ~ 4.50
Mo (％): 0.30 ~ 0.60
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: Bars,flat bar, and forgings
Mo (％): 0.30 ~ 0.60
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: Bars,flat bar, and forgings
Heat treatment condition:
Annealed condition: heat to 680°C followed by slow cooling.
Brinell Hardness:285
Brinell Hardness:285
Air cool from 875°C. Sub-zero treatment (-75°C). Temper at 200°C.
UTS:1900 N/mm2
0.2 % Yield strength:1500 N/mm2
Elongation (5d):10 %
Impact strength KCU:50J
UTS:1900 N/mm2
0.2 % Yield strength:1500 N/mm2
Elongation (5d):10 %
Impact strength KCU:50J
Air cool from 875°C. Temper at 650°C.
UTS:1050 N/mm2
0.2 % Yield strength:900 N/mm2
Elongation (5d):18 %
Impact strength KCU:110J
UTS:1050 N/mm2
0.2 % Yield strength:900 N/mm2
Elongation (5d):18 %
Impact strength KCU:110J
MELTING PROCESS & APPLICATION
This alloy is generally smelt in EAF, VOD or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
FORMS & DIMENSIONS
Round bar: 5.5mm to 400mm
Square bar / Flat bar: 10mm to 550mm
Wire rod: 1.0mm to 13.0mm
Steel strip: THK0.5 ~ 3.0mm, Width 10 ~ 300mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
This alloy is generally smelt in EAF, VOD or VIM + Electroslag remelting (ESR). For a purpose of superior quality, it should be smelt via technology of vacuum refining or by agreement.
FORMS & DIMENSIONS
Round bar: 5.5mm to 400mm
Square bar / Flat bar: 10mm to 550mm
Wire rod: 1.0mm to 13.0mm
Steel strip: THK0.5 ~ 3.0mm, Width 10 ~ 300mm
Length: Fixed length or random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com.
Hot search：E35NCD16H