Specifications 65MnCr4 Data sheet, Stocklist 65MnCr4 Chemical, Inventory Suppliers 65MnCr4 Properties from Steelmaking, ESR melted, Blooming, Hot forging rolling, Heat treat, Straightened, 100% Ultrasonic test, Cold working or rough turned machining. Technical specifications - ISO 4597 - 2001. We also possess the advanced precision machining equipments for catering for your different special requirements.
MATERIAL DATA SHEET - Grade 65MnCr4
MATERIAL CATEGORY - Cold work alloy tool steel
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000, DIN 17350
MELTING PROCESS - EAF + AOD / + ESR
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
Official Test Certificate - issued by TUV - SGS - BV
CHEMICAL COMPOSITION ( Mass Weight % )
C (％): 0.60 ~ 0.68
Si (％): 0.30 ~ 0.50
Mn (％): 1.10 ~ 1.20
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 0.60 ~ 0.80
Mo (％): -
V (％): -
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1000 ~ 800
Annealing temperature /℃: 700 ~ 720
Hardness after annealing ≤HBW: 220
Quenching temperature /℃: 770 ~ 800
Cooling medium: water
Common tempering temperature /℃: 180 ~ 200
Hardness after tempering at temperature HRC|100℃: 66
Hardness after tempering at temperature HRC|200℃: 63
Hardness after tempering at temperature HRC|300℃: 57
Hardness after tempering at temperature HRC|400℃: 50
AVAILABLE SHAPES
Round bar / flat bar / plate / tube / forgings / strip / valve body
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
MATERIAL CATEGORY - Cold work alloy tool steel
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000, DIN 17350
MELTING PROCESS - EAF + AOD / + ESR
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
Official Test Certificate - issued by TUV - SGS - BV
CHEMICAL COMPOSITION ( Mass Weight % )
C (％): 0.60 ~ 0.68
Si (％): 0.30 ~ 0.50
Mn (％): 1.10 ~ 1.20
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 0.60 ~ 0.80
Mo (％): -
V (％): -
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1000 ~ 800
Annealing temperature /℃: 700 ~ 720
Hardness after annealing ≤HBW: 220
Quenching temperature /℃: 770 ~ 800
Cooling medium: water
Common tempering temperature /℃: 180 ~ 200
Hardness after tempering at temperature HRC|100℃: 66
Hardness after tempering at temperature HRC|200℃: 63
Hardness after tempering at temperature HRC|300℃: 57
Hardness after tempering at temperature HRC|400℃: 50
AVAILABLE SHAPES
Round bar / flat bar / plate / tube / forgings / strip / valve body
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
FORMS AND DIMENSIONS
Round bar (Diameter): 5.5 to 650mm
Steel strip: THK0.15 ~ 2.50 X W8.0 ~ 600mm
Flat bar (Thickness X width): 10 ~ 350 X 15 ~ 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
TYPICAL APPLICATIONS
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Round bar (Diameter): 5.5 to 650mm
Steel strip: THK0.15 ~ 2.50 X W8.0 ~ 600mm
Flat bar (Thickness X width): 10 ~ 350 X 15 ~ 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
TYPICAL APPLICATIONS
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Hot search：65MnCr4