1.2326
2021-10-06 09:05:06 Origin： Remark：0 Click：
Specifications 1.2326 Data sheet, Stocklist 1.2326 Chemical, Inventory Suppliers 1.2326 Properties from Steelmaking, ESR melted, Blooming, Hot forging % rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or rough turned machining. Technical specifications - ISO 4597 - 2001. We also possess the advanced precision machining equipments for catering for your different special requirements.
MATERIAL DATA SHEET - Grade 1.2326
MATERIAL CATEGORY - Cold work alloy tool steel
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000, DIN 17350
MELTING PROCESS - EAF + AOD / + ESR
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
Official Test Certificate - issued by TUV - SGS - BV
CHEMICAL COMPOSITION ( Mass Weight % )
Hot working tenperature /℃: 1000 ~ 800
Annealing temperature /℃: 690 ~ 730
Hardness after annealing ≤HBW: 250
Quenching temperature /℃: 840 ~ 860
Cooling medium: liquid
MATERIAL CATEGORY - Cold work alloy tool steel
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000, DIN 17350
MELTING PROCESS - EAF + AOD / + ESR
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
Official Test Certificate - issued by TUV - SGS - BV
CHEMICAL COMPOSITION ( Mass Weight % )
C (％): 0.40 ~ 0.50
Si (％): 0.15 ~ 0.35
Mn (％): 0.60 ~ 0.90
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 1.30 ~ 1.60
Mo (％): 0.60 ~ 0.85
V (％): 0.25 ~ 0.35
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESSSi (％): 0.15 ~ 0.35
Mn (％): 0.60 ~ 0.90
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 1.30 ~ 1.60
Mo (％): 0.60 ~ 0.85
V (％): 0.25 ~ 0.35
Hot working tenperature /℃: 1000 ~ 800
Annealing temperature /℃: 690 ~ 730
Hardness after annealing ≤HBW: 250
Quenching temperature /℃: 840 ~ 860
Cooling medium: liquid
General tempering temp./℃: 180 ~ 300
Hardness after tempering at temperature HRC|100℃: 59
Hardness after tempering at temperature HRC|200℃: -
Hardness after tempering at temperature HRC|300℃: -
Hardness after tempering at temperature HRC|400℃: -
Hardness after tempering at temperature HRC|200℃: -
Hardness after tempering at temperature HRC|300℃: -
Hardness after tempering at temperature HRC|400℃: -
AVAILABLE SHAPES
Round bar / flat bar / plate / tube / forgings / valve body
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
Round bar / flat bar / plate / tube / forgings / valve body
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
FORMS AND DIMENSIONS
Round bar (Diameter): 5.5 to 450mm
Steel strip: THK0.15 ~ 2.50 X W8.0 ~ 560mm
Flat bar (Thickness X width): 10 ~ 350 X 15 ~ 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
TYPICAL APPLICATIONS
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Round bar (Diameter): 5.5 to 450mm
Steel strip: THK0.15 ~ 2.50 X W8.0 ~ 560mm
Flat bar (Thickness X width): 10 ~ 350 X 15 ~ 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
TYPICAL APPLICATIONS
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：1.2326