Specification X40CrMoV5-1 Data sheet, Inventory X40CrMoV5-1 Chemical, Stocklist X40CrMoV5-1 Properties from Steel melting, ESR melted, Blooming, Hot forging / Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or rough turned machining. Technical specifications - ISO 4597 - 2001. We also possess the advanced precision machining equipments for catering for your different special requirements.
MATERIAL DATA SHEET - Grade X40CrMoV5-1
MATERIAL CATEGORY - Hot work alloy tool steel
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000, DIN 17350
MELTING PROCESS - EAF + AOD / + ESR
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
Official Test Certificate - issued by TUV - SGS - BV
CHEMICAL COMPOSITION ( Mass Weight % )
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1100 ~ 900
Annealing temperature /℃: 750 ~ 780
Hardness after annealing ≤HBW: 235
Quenching temperature /℃: 1020
Cooling medium: liquid / air
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000, DIN 17350
MELTING PROCESS - EAF + AOD / + ESR
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
Official Test Certificate - issued by TUV - SGS - BV
CHEMICAL COMPOSITION ( Mass Weight % )
C (％): 0.36 ~ 0.44
Si (％): 0.80 ~ 1.20
Si (％): 0.80 ~ 1.20
Mn (％): 0.20 ~ 0.50
P (％)≤: 0.030
S (％)≤: 0.030
Cr (%): 4.80 ~ 5.50
Mo (％): 1.20 ~ 1.50
Ni (%): -
V (%): 0.85 ~ 1.15
P (％)≤: 0.030
S (％)≤: 0.030
Cr (%): 4.80 ~ 5.50
Mo (％): 1.20 ~ 1.50
Ni (%): -
V (%): 0.85 ~ 1.15
Hot working tenperature /℃: 1100 ~ 900
Annealing temperature /℃: 750 ~ 780
Hardness after annealing ≤HBW: 235
Quenching temperature /℃: 1020
Cooling medium: liquid / air
General tempering temp./℃: 550
Hardness after tempering at temperature HRC|100℃: 54
Hardness after tempering at temperature HRC|200℃: -
Hardness after tempering at temperature HRC|300℃: -
Hardness after tempering at temperature HRC|400℃: -
Hardness after tempering at temperature HRC|200℃: -
Hardness after tempering at temperature HRC|300℃: -
Hardness after tempering at temperature HRC|400℃: -
AVAILABLE SHAPES
Round bar / flat bar / plate / tube / forgings / valve body
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
Round bar / flat bar / plate / tube / forgings / valve body
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
FORMS AND DIMENSIONS AVAILABLE
Round bar (Diameter): 5.5 to 600mm
Steel strip: THK0.15 ~ 2.50 X W8.0 ~ 200mm
Flat bar (Thickness X width): 10 ~ 350 X 15 ~ 1200mm
Length: Fixed length or random length or based on the customer's special requirement.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
TYPICAL APPLICATIONS
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Round bar (Diameter): 5.5 to 600mm
Steel strip: THK0.15 ~ 2.50 X W8.0 ~ 200mm
Flat bar (Thickness X width): 10 ~ 350 X 15 ~ 1200mm
Length: Fixed length or random length or based on the customer's special requirement.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
TYPICAL APPLICATIONS
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools