Specifications 60CrMoV13-5 Round bar, Flat bar, Inventory 60CrMoV13-5 Steel melting, ESR melted, Blooming, Hot forging / Hot rolling, Heat treatment.
MATERIAL DATA SHEET - Grade 60CrMoV13-5
MATERIAL CATEGORY - Cold work alloy tool steel
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000, DIN 17350
MELTING PROCESS - EAF + AOD / + ESR
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
Official Test Certificate - issued by TUV - SGS - BV
CHEMICAL COMPOSITION (mass weight - % )
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1100 ~ 900
Annealing temperature /℃: 800 ~ 840
Hardness after annealing ≤HBW: 255
Quenching temperature /℃: 950 ~ 1010
Cooling medium: liquid / air
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000, DIN 17350
MELTING PROCESS - EAF + AOD / + ESR
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
Official Test Certificate - issued by TUV - SGS - BV
CHEMICAL COMPOSITION (mass weight - % )
Carbon, C (％): 0.50 ~ 0.70
Silicon, Si (％): ≤ 0.40
Silicon, Si (％): ≤ 0.40
Manganese, Mn (％): 0.20 ~ 0.80
Phosphorus, P (％)≤: 0.025
Sulfur, S (％)≤: 0.025
Chromium, Cr (%): 3.00 ~ 3.50
Molybdenum, Mo (％): 0.25 ~ 0.75
Nickel, Ni (%): ≤ 0.50
Phosphorus, P (％)≤: 0.025
Sulfur, S (％)≤: 0.025
Chromium, Cr (%): 3.00 ~ 3.50
Molybdenum, Mo (％): 0.25 ~ 0.75
Nickel, Ni (%): ≤ 0.50
Vanadium, V (%): 0.05 ~ 0.18
Hot working tenperature /℃: 1100 ~ 900
Annealing temperature /℃: 800 ~ 840
Hardness after annealing ≤HBW: 255
Quenching temperature /℃: 950 ~ 1010
Cooling medium: liquid / air
General tempering temp./℃: 510
Hardness after tempering at temperature HRC|100℃: 53
Hardness after tempering at temperature HRC|200℃: -
Hardness after tempering at temperature HRC|300℃: -
Hardness after tempering at temperature HRC|400℃: -
Hardness after tempering at temperature HRC|200℃: -
Hardness after tempering at temperature HRC|300℃: -
Hardness after tempering at temperature HRC|400℃: -
FORMS AND DIMENSIONS AVAILABLE
Round bar (Diameter): 5.5 to 500mm
Steel strip: THK0.15 ~ 2.50 X W8.0 ~ 200mm
Flat bar (Thickness X width): 10 ~ 350 X 15 ~ 650mm
Length: Fixed length or random length or based on the customer's special requirement.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Steel strip: THK0.15 ~ 2.50 X W8.0 ~ 200mm
Flat bar (Thickness X width): 10 ~ 350 X 15 ~ 650mm
Length: Fixed length or random length or based on the customer's special requirement.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
TECHNICAL SALES ASSISTANCE & SERVICE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：60CrMoV13-5