Specifications 102Cr6 Chemical, Inventory 102Cr6 Datasheet, Suppliers 102Cr6 Properties from Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or rough turned machining. Technical specifications - ISO 4597 - 2001. We also possess the advanced precision machining equipments for catering for your different special requirements.
TOOL STEEL DATASHEET - DIN 102Cr6
Material category - Cold work alloy tool steel
TYPICAL APPLICATIONS
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
PRODUCT DESCRIPTION
The alloy is usually produced by EAF /VD /LF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright in the softened condition.
Final heat treatment - heat treatment / QT
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000 , DIN 17350 (1980)
AVAILABLE SHAPES
Round bar / flat bar / square bar / plate
Bright - peeled + polishing, centerless grinding
Forged - ring /tube /pipe casing /discs /shaft
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 10mm to 700mm
Plate / Sheet steel / Steel strip: 0.5mm to 610mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes.
CHEMICAL COMPOSITION ( Mass Weight % )
C (％): 0.95 ~ 1.10
Si (％): 0.15 ~ 0.35
Mn (％): 0.25 ~ 0.40
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 1.35 ~ 1.65
Mo (％): -
V (％): -
Si (％): 0.15 ~ 0.35
Mn (％): 0.25 ~ 0.40
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 1.35 ~ 1.65
Mo (％): -
V (％): -
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1050～850
Annealing temperature /℃: 740～770
Hardness after annealing ≤HBW: 230
Quenching temperature /℃: 820～850
Cooling medium: water / oil
Common tempering temperature /℃: 100～180
Hardness after tempering at temperature HRC|100℃: 64
Hardness after tempering at temperature HRC|200℃: 61
Hardness after tempering at temperature HRC|300℃: 56
Hardness after tempering at temperature HRC|400℃: 50
Annealing temperature /℃: 740～770
Hardness after annealing ≤HBW: 230
Quenching temperature /℃: 820～850
Cooling medium: water / oil
Common tempering temperature /℃: 100～180
Hardness after tempering at temperature HRC|100℃: 64
Hardness after tempering at temperature HRC|200℃: 61
Hardness after tempering at temperature HRC|300℃: 56
Hardness after tempering at temperature HRC|400℃: 50
TECHNICAL SALES ASSISTANCE