X16CrNiSi20-12
2023-03-12 16:57:02 Origin： Remark：0 Click：
Hot work tool steel X16CrNiSi20-12 Round bar, flat bar, plate ESR melted, Hot forging / Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or machining.
MATERIAL SPECIFICATIONS - Grade X16CrNiSi20-12
MATERIAL CATEGORY - Hot work alloy tool steel
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000, DIN 17350
MELTING PROCESS - EAF + VD + LF / BEF + ESR
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
Official Test Certificate - issued by TUV - SGS - BV
MAIN CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): ≤ 0.20
MATERIAL CATEGORY - Hot work alloy tool steel
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000, DIN 17350
MELTING PROCESS - EAF + VD + LF / BEF + ESR
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
Official Test Certificate - issued by TUV - SGS - BV
MAIN CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): ≤ 0.20
Silicon, Si (％): 1.80 ~ 2.30
Manganese, Mn (％): 2.00
Phosphorus, P (％)≤: 0.035
Sulfur, S (％)≤: 0.025
Chromium, Cr (％): 19.0 ~ 21.0
Nickel, Ni (％): 11.0 ~ 13.0
Sulfur, S (％)≤: 0.025
Chromium, Cr (％): 19.0 ~ 21.0
Nickel, Ni (％): 11.0 ~ 13.0
Molybdenum, Mo (%): -
Ferrum, Fe (%): balance.
MECHANICAL PROPERTIES - HEAT TREATMENT CYCLE - HARDNESS
Hot working tenperature /℃: 1050 ~ 850
Annealing temperature /℃: 1010 ~ 1150
Hardness after annealing ≤HBW: 207
Quenching temperature /℃: -
Cooling medium: air or oil
Common tempering temperature /℃: 180 ~ 350
Hardening value after tempering at temperature /MPa | 100℃: HRC 55
TYPICAL APPLICATIONS
Cutting tools. Mechanical parts, Air hammer tools. Piercing tools.
ADVANTAGE & SUPERIOR SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Round bar (Diameter): 5.5 to 550mm
Flat bar (Thickness X width): 10 ~ 350 X 15 ~ 1000 X Lmm
Heavy plate (Thickness X width): 40 ~ 400 X 50 ~ 1100 X Lmm
Length: fixed length, random length or based on the customer's special requirement.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
MECHANICAL PROPERTIES - HEAT TREATMENT CYCLE - HARDNESS
Hot working tenperature /℃: 1050 ~ 850
Annealing temperature /℃: 1010 ~ 1150
Hardness after annealing ≤HBW: 207
Quenching temperature /℃: -
Cooling medium: air or oil
Common tempering temperature /℃: 180 ~ 350
Hardening value after tempering at temperature /MPa | 100℃: HRC 55
TYPICAL APPLICATIONS
Cutting tools. Mechanical parts, Air hammer tools. Piercing tools.
ADVANTAGE & SUPERIOR SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Round bar (Diameter): 5.5 to 550mm
Flat bar (Thickness X width): 10 ~ 350 X 15 ~ 1000 X Lmm
Heavy plate (Thickness X width): 40 ~ 400 X 50 ~ 1100 X Lmm
Length: fixed length, random length or based on the customer's special requirement.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：X16CrNiSi20-12
Previous page：AMS 5685
Last page：AMS 5686 Wire rod, round bar, Forgings