T55Cr3V2
2023-09-22 09:27:07 Origin： Remark：0 Click：
IS 1570 - 6 Material Specification Tool Steel T55Cr3V2 Round bar, Flat bar, Plate T55Cr3V2 Heat treat, Cold machined.
TECHNICAL SPECIFICATION DATASHEET - Grade T55Cr3V2
Material Category - High carbon cold working tool steel
Material Specifications - IS 1570 - 6 (1996 / 2001 )
Special Melting Process - EAF + VD + LF / BEF + ESR
H S CODE For Customs: 7228 4000 / 7228 5000 / 7228 6000
READY STOCK ON HAND - Round bar diameter 15 ~ 150mm
Official Test Certificate - issued by TUV - SGS - BV
Material Category - High carbon cold working tool steel
Material Specifications - IS 1570 - 6 (1996 / 2001 )
Special Melting Process - EAF + VD + LF / BEF + ESR
H S CODE For Customs: 7228 4000 / 7228 5000 / 7228 6000
READY STOCK ON HAND - Round bar diameter 15 ~ 150mm
Official Test Certificate - issued by TUV - SGS - BV
MAIN CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.50 ~ 0.60
Silicon, Si (％): 0.10 ~ 0.35
Manganese, Mn (％): 0.60 ~ 0.80
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.025
Chromium, Cr (％): 0.60 ~ 0.80
Molybdenum, Mo (%): -
Vanadiuml, V (％): 0.10 ~ 0.20
Ferrum, Fe (%): Balance.
MECHANICAL PROPERTIES - HEAT TREATMENT CYCLE
Hot working tenperature /℃: 1090 ~ 950
Annealing temperature /℃: -
Quenching temperature /℃: 830 ~ 860
Cooling medium: oil
Common tempering temperature /℃: 200 ~ 500
Forms: Round bar, flat bar, plate, shaft
Tensile strength, σb/≥ MPa: 1400 ~ 1700
Yield strength, σ0.2/MPa: 1200
Elongation, δ ≥(％): 6.0
Reduction of area, ф ≥ (％): -
Hardness via annealing heat treatment /HBW: 230 max.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.