TECHNICAL SPECIFICATION - Grade 95V4 & DIN 1.2835
MATERIAL CATEGORY - Cold work alloy tool steel 
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000, DIN 17350
MELTING PROCESS: EAF + VD + LF / BEF + ESR
H S CODE For Customs: 7228 4000 / 7228 5000 / 7228 6000
Official Test Certificate - issued by TUV - SGS -  BV
MAIN CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％):  0.90 ~ 1.00
Silicon, Si (％):  0.10 ~ 0.35
Manganese, Mn (％):  0.30 ~ 0.50
Phosphorus, P (％) ≤:  0.030
Sulfur, S (％) ≤:  0.015
Chromium, Cr (％):  -
Vanadium, V (％):  0.35 ~ 0.45
Ferrum, Fe (%):  remainder
MECHANICAL PROPERTIES - HEAT TREATMENT CYCLE - HARDNESS
Hot working tenperature /℃:  1100 ~ 900
Annealing temperature /℃:  760 ~ 780
Hardness after annealing ≤HBW:  255
Quenching temperature /℃:  800 ~ 950
Cooling medium:  oil
Common tempering temperature /℃:   180 ~ 320
Hardening value after tempering at temperature /MPa | 100℃: -
Hardening value after tempering at temperature /MPa | 200℃:  -
Hardening value after tempering at temperature /MPa | 300℃:  -
Hardening value after tempering at temperature /MPa | 400℃:  HRC 61
ADVANTAGE & SUPERIOR SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Round bar (diameter): 5.5 to 500mm
Flat bar (Thickness X width): 10 ~ 400 X 15 ~ 600 X Lmm
Heavy plate (Thickness X width): 40 ~ 300 X 50 ~ 1200 X Lmm
Length: fixed length, random length or based on the customer's special requirement.