※DATA SHEET - ALLOY TOOL STEEL DIN54NiCrMoV6 / W-Nr 1.2711※※ MATERIALCATEGORY: Cold work alloytool steelCold wor...
※ DATA SHEET - ALLOY TOOL STEEL DIN 54NiCrMoV6 / W-Nr 1.2711 ※
※ MATERIAL CATEGORY: Cold work alloy tool steel
Cold work die includes cold punching mould, wire-drawing die, drawing die, coining die, thread rolling die, cold heading die, cold extrusion die, Based on the working condition, cold work die should have the high hardness, strength, abrasion resistance, toughness, hardenability, quenching degree, and other processing property. This kind of alloy tool steel belongs to high carbon alloy steel (carbon mass fraction is over 0.80%), Chromium is key element of alloy with mass fraction below 5% generally.
※ MATERIAL SPECIFICATIONS
EN ISO 4957: 2000 , DIN 17350 (1980)
※ PRODUCT DESCRIPTION
The alloy is usually produced by EAF /VD /LF /IFF followed by electroslag refining (ESR) if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the
buyers' requirements.
Bars are usually supplied bright (peeling or centreless grinding) in the softened = SA condition.
Final heat treatment - heat treatment / spheroidizing annealing
※ AVAILABLE SHAPES
Black bar /Flat bar /Square bar
Bright - peeled + polishing /centerless grinding / peeled + slidabrading
Forged - ring /tube /pipe casing /discs /shaft
※ CHEMICAL COMPOSITION (WEIGHT %)
C(％): 0.50～0.60
Si(％): 0.15～0.35
Mn(％): 0.50～0.80
P(％)≤: 0.025
S(％)≤: 0.035
Cr(％): 0.60～0.80
Mo(％): 0.25～0.35
V(％): 0.08～0.12
Other(％): Ni 1.50～1.80
Si(％): 0.15～0.35
Mn(％): 0.50～0.80
P(％)≤: 0.025
S(％)≤: 0.035
Cr(％): 0.60～0.80
Mo(％): 0.25～0.35
V(％): 0.08～0.12
Other(％): Ni 1.50～1.80
※ MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1050～850
Annealing temperature /℃: 650～700
Hardness after annealing ≤HBW: 225
Annealing temperature /℃: 650～700
Hardness after annealing ≤HBW: 225
Quenching temperature /℃: 830 ~ 870
Cooling medium: oil
Common tempering temperature /℃: 620~700
Hardness after tempering at temperature HRC|100℃: 56
Cooling medium: oil
Common tempering temperature /℃: 620~700
Hardness after tempering at temperature HRC|100℃: 56
Hardness after tempering at temperature HRC|200℃: 54
Hardness after tempering at temperature HRC|300℃: 51
Hardness after tempering at temperature HRC|400℃: 47
Hardness after tempering at temperature HRC|300℃: 51
Hardness after tempering at temperature HRC|400℃: 47
※ HEAT TREATTMENT PRACTICE
The preheating of measuring and cutting tool steel is spheroidizing annealing, final heat treatment is quenching + low temperature tempering and hardness after heat treatment can reach 60~65HRC. When heat treat tool steel grades consideration should be given to hardening temperature, including ratio of heating, cooling and soaking times which will differ due to factors such as the shape and size of each chemical component. Other considerations during heat treatment include the type of furnace, quenching medium and work piece transfer facilities.
The preheating of measuring and cutting tool steel is spheroidizing annealing, final heat treatment is quenching + low temperature tempering and hardness after heat treatment can reach 60~65HRC. When heat treat tool steel grades consideration should be given to hardening temperature, including ratio of heating, cooling and soaking times which will differ due to factors such as the shape and size of each chemical component. Other considerations during heat treatment include the type of furnace, quenching medium and work piece transfer facilities.
※ TYPICAL APPLICATIONS
Alloy tool steel is widely used to produce the cutting tool, cold/heat distortion mould and measuring implements,
and further to manufacture the piston, valve, valve seat of fuel pump of diesel engine.
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
※ INVENTORY - hot forged bar/disc
Diameter: 60mm
Quantity: 42kg
Diameter: 60mm
Quantity: 42kg
※ TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
Round bar / Wire rod (Diameter): 0.50mm to 3000mm
Square bar / Flat bar: 3mm to 2000mm
Plate / Sheet steel / Steel strip: 0.1mm to 2500mm
Width: 8mm to 2500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Pipes / Tubings: OD 3-219 mm, with wall thickness ranging from 0.50 to 35 mm.