6CrMnSi2Mo1V
2024-08-19 09:09:10 Origin： Remark：0 Click：
GB/T 1299-2014 Material Specification of Impact Resisitant Steel 6CrMnSi2Mo1V Round bar, Flat bar, Plate, Wire Rod 6CrMnSi2Mo1V Heat treatment
RAW MATERIAL DATASHEET - GB 6CrMnSi2Mo1V
Material Specifications - GB/T 1299-2014
Special Melting Process - EAF + VD + LF / BEF
H S Code For Customs: 7228 4000 / 7228 5000 / 7228 6000
Available Stock on hand - Round bar diameter 50 ~ 160mm
Typical applications - Cutting tools. Mechanical parts, Air hammer tools. Piercing tools.
PROFILES & DIMENSIONS AVAILABLE
Round bar (diameter): 5.5 ~ 300mm
Flat bar (thickness X width): 10 ~ 200 X 15 ~ 600 X L mm
Sheet / plate (thickness X width): 1.0 ~ 200 X 10 ~ 900 X L mm
Forging piece: stepped shafts and other different shapes based on OEM.
Third party inspection service.
Export packing / Export documents.
CNC saw cutting.
Marking by stamping or printing.
Transport by Track, Sea, Courier (FedEx, UPS, DHL) and Air Cargo.
Round bar (diameter): 5.5 ~ 300mm
Flat bar (thickness X width): 10 ~ 200 X 15 ~ 600 X L mm
Sheet / plate (thickness X width): 1.0 ~ 200 X 10 ~ 900 X L mm
Forging piece: stepped shafts and other different shapes based on OEM.
Third party inspection service.
Export packing / Export documents.
CNC saw cutting.
Marking by stamping or printing.
Transport by Track, Sea, Courier (FedEx, UPS, DHL) and Air Cargo.
MAIN CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.55 ~ 0.65
Silicon, Si (％): 1.75 ~ 2.25
Manganese, Mn (％): 0.60 ~ 1.00
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.025
Chromium, Cr (％): 0.10 ~ 0.50
Tungsten, W (%): -
Molybdenum, Mo (%): 0.20 ~ 1.35
Vanadium, V (%): 0.15 ~ 0.25
Ferrum, Fe (%): balance.
Carbon, C (％): 0.55 ~ 0.65
Silicon, Si (％): 1.75 ~ 2.25
Manganese, Mn (％): 0.60 ~ 1.00
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.025
Chromium, Cr (％): 0.10 ~ 0.50
Tungsten, W (%): -
Molybdenum, Mo (%): 0.20 ~ 1.35
Vanadium, V (%): 0.15 ~ 0.25
Ferrum, Fe (%): balance.
MECHANICAL PROPERTIES - HEAT TREATMENT PRACTICE
Annealing temperature /℃: -
Quenching temperature /℃: preheating 667℃, then 900 ℃ holding time 5 ~ 15 min
Cooling medium: oil.
Common tempering temperature /℃: 58 ~ 204
Hardness via tempering Temp. HRC: 57 Min.
Hardness via annealing heat treatment / HBW: 229 Max.
Common tempering temperature /℃: 58 ~ 204
Hardness via tempering Temp. HRC: 57 Min.
Hardness via annealing heat treatment / HBW: 229 Max.
TECHNICAL SALES ASSISTANCE & SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you are interested in our products or services, or would like to learn more about us, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers or sales department.
Hot search：