EN ISO 4957 Specification 60MnSiCr4 Round bar, Flat bar, Forgings 60MnSiCr4 Properties, hot forging, hot rolling, heat treatment, cold working.
MATERIAL DATA SHEET - 60MnSiCr4
MATERIAL CATEGORY - Cold work alloy tool steel
Cold work die includes cold punching mould, wire-drawing die, drawing die, coining die, thread rolling die, cold heading die, cold extrusion die, Based on the working condition, cold work die should have the high hardness, strength, abrasion resistance, toughness, hardenability, quenching degree, and other processing property. This kind of alloy tool steel belongs to high carbon alloy steel (carbon mass fraction is over 0.80%), Chromium is key element of alloy with mass fraction below 5% generally.
MATERIAL SPECIFICATIONS - EN ISO 4957 : 2000, DIN 17350 (1980)
PRODUCT DESCRIPTION
The alloy is usually produced by EAF /VD /LF / IFF followed by electroslag refining (ESR) if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different level according to the buyers' requirements.
Bars are usually supplied bright (peeling or centreless grinding) in the softened = SA condition.
Final heat treatment - heat treatment / spheroidizing annealing
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.58 ~ 0.65
Silicon, Si (％): 0.80 ~ 1.00
Manganese, Mn (％): 0.80 ~ 1.20
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 0.20 ~ 0.40
Molybdneum, Mo (％): -
Vanadium, V (％): -
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Silicon, Si (％): 0.80 ~ 1.00
Manganese, Mn (％): 0.80 ~ 1.20
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 0.20 ~ 0.40
Molybdneum, Mo (％): -
Vanadium, V (％): -
MECHANICAL PROPERTIES - HOT WORKING, HEAT TREATMENT AND HARDNESS
Hot working tenperature /℃: 1050 ~ 850
Annealing temperature /℃: 680 ~ 720
Hardness after annealing ≤HBW: 220
Annealing temperature /℃: 680 ~ 720
Hardness after annealing ≤HBW: 220
Quenching temperature /℃: 820 ~ 850
Cooling medium: oil
Common tempering temperature /℃: 300~500
Hardness after tempering at temperature HRC|100℃: 61
Cooling medium: oil
Common tempering temperature /℃: 300~500
Hardness after tempering at temperature HRC|100℃: 61
Hardness after tempering at temperature HRC|200℃: 59
Hardness after tempering at temperature HRC|300℃: 57
Hardness after tempering at temperature HRC|400℃: 52
Hardness after tempering at temperature HRC|400℃: 52
HEAT TREATTMENT PRACTICE
The preheating of measuring and cutting tool steel is spheroidizing annealing, final heat treatment is quenching + low temperature tempering and hardness after heat treatment can reach 60~65HRC. When heat treat tool steel grades consideration should be given to hardening temperature, including ratio of heating, cooling and soaking times which will differ due to factors such as the shape and size of each chemical component. Other considerations during heat treatment include the type of furnace, quenching medium and work piece transfer facilities.
The preheating of measuring and cutting tool steel is spheroidizing annealing, final heat treatment is quenching + low temperature tempering and hardness after heat treatment can reach 60~65HRC. When heat treat tool steel grades consideration should be given to hardening temperature, including ratio of heating, cooling and soaking times which will differ due to factors such as the shape and size of each chemical component. Other considerations during heat treatment include the type of furnace, quenching medium and work piece transfer facilities.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email us: sales@ccsteels.com
PRODUCT PROFILE & DIMENSIONS
Round bar / Disc (diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 600mm
Plate / Sheet steel / Steel strip: 0.1mm to 500mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.