1.2564 / 30WCrV15-1
2014-11-13 19:31:04 Origin： Remark：0 Click：
Description 1.2564 Suppliers, Inventory 1.2564 Stocklist, Ex-stock 1.2564 Specifications - ISO 4597 Properties from Steel melting, ESR melted, Blooming, Hot forging / Hot rolling, Heat treated, Straightening, 100% Ultrasonic test, Cold working or rough turned machining. Technical specifications - ISO 4597 - 2001. We also possess the advanced precision machining equipments for catering for your different special requirements.
MATERIAL DATA SHEET - Grade 1.2564 & 30WCrV15-1
MATERIAL CATEGORY - Hot work alloy tool steel
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000, DIN 17350
MELTING PROCESS - EAF / AOD / + ESR
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
Official Test Certificate - issued by TUV - SGS - BV
CHEMICAL COMPOSITION ( Mass Weight % )
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000, DIN 17350
MELTING PROCESS - EAF / AOD / + ESR
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
Official Test Certificate - issued by TUV - SGS - BV
CHEMICAL COMPOSITION ( Mass Weight % )
C (％): 0.25 ~ 0.35
Si (％): 0.80 ~ 1.10
Mn (％): 0.30 ~ 0.50
P (％)≤: 0.035
S (％)≤: 0.035
Cr (％): 0.90 ~ 1.20
Mo (％): -
V (％): 0.15 ~ 0.20
W (%): 3.50 ~ 4.00
Si (％): 0.80 ~ 1.10
Mn (％): 0.30 ~ 0.50
P (％)≤: 0.035
S (％)≤: 0.035
Cr (％): 0.90 ~ 1.20
Mo (％): -
V (％): 0.15 ~ 0.20
W (%): 3.50 ~ 4.00
HOT WORKING, HEAT TREATMENT CYCLE AND HARDNESS
Hot working tenperature /℃: 1050 ~ 850
Annealing temperature /℃: 750 ~ 780
Hardness after annealing ≤HBW: 230
Annealing temperature /℃: 750 ~ 780
Hardness after annealing ≤HBW: 230
Quenching temperature /℃: 1000 ~ 1050
Cooling medium: oil
Cooling medium: oil
Common tempering temperature /℃: 450 ~ 650
Hardening value after tempering at temperature /MPa |400℃: -
Hardening value after tempering at temperature /MPa |400℃: -
Hardening value after tempering at temperature /MPa |500℃: 1520
Hardening value after tempering at temperature /MPa |600℃: 1370
Hardening value after tempering at temperature /MPa |650℃: 1270
Hardening value after tempering at temperature /MPa |650℃: 1270
AVAILABLE SHAPES
Round bar / flat bar / hollow bar / plate / forgings
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
Round bar / flat bar / hollow bar / plate / forgings
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
FORMS AND DIMENSIONS AVAILABLE
Round bar (Diameter): 5.5 to 620mm
Steel strip: THK0.15 ~ 2.50 X W5.0 ~ 200mm
Flat bar (Thickness X width): 10 ~ 350 X 15 ~ 650mm
Length: Fixed length or random length or based on the customer's special requirement.
TYPICAL APPLICATIONS
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
TECHNICAL SALES ASSISTANCE & SERVICE
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Round bar (Diameter): 5.5 to 620mm
Steel strip: THK0.15 ~ 2.50 X W5.0 ~ 200mm
Flat bar (Thickness X width): 10 ~ 350 X 15 ~ 650mm
Length: Fixed length or random length or based on the customer's special requirement.
TYPICAL APPLICATIONS
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
TECHNICAL SALES ASSISTANCE & SERVICE
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.