1.2567 / 30WCrV17-2
2014-11-19 19:09:09 Origin： Remark：0 Click：
Description 1.2567 Suppliers, Inventory 1.2567 Stocklist, Ex-stock 1.2567 Bar Specifications - ISO 4597 Properties from Steel melting, ESR melted, Blooming, Hot forging / Hot rolling, Heat treated, Straightening, 100% Ultrasonic test, Cold working or rough turned machining. Technical specifications - ISO 4597 - 2001. We also possess the advanced precision machining equipments for catering for your different special requirements.
MATERIAL DATA SHEET - Grade 1.2567 & 30WCrV17-2
MATERIAL CATEGORY - Hot work alloy tool steel
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000, DIN 17350
MELTING PROCESS - EAF / AOD / + ESR
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
Official Test Certificate - issued by TUV - SGS - BV
CHEMICAL COMPOSITION ( Mass Weight % )
MATERIAL SPECIFICATIONS - EN ISO 4957: 2000, DIN 17350
MELTING PROCESS - EAF / AOD / + ESR
H S CODE For Customs - 7228 4000 / 7228 5000 / 7228 6000
Official Test Certificate - issued by TUV - SGS - BV
CHEMICAL COMPOSITION ( Mass Weight % )
C (％): 0.25 ~ 0.35
Si (％): 0.15 ~ 0.30
Mn (％): 0.20 ~ 0.40
P (％)≤: 0.035
S (％)≤: 0.035
Cr (％): 2.20 ~ 2.50
Mo (％): -
V (％): 0.50 ~ 0.70
W (％): 4.00 ~ 4.50
Si (％): 0.15 ~ 0.30
Mn (％): 0.20 ~ 0.40
P (％)≤: 0.035
S (％)≤: 0.035
Cr (％): 2.20 ~ 2.50
Mo (％): -
V (％): 0.50 ~ 0.70
W (％): 4.00 ~ 4.50
PROPERTIES - HOT WORKING, HEAT TREATMENT CYCLE
Hot working tenperature /℃: 1050 ~ 850
Annealing temperature /℃: 760 ~ 800
Hardness after annealing ≤HBW: 240
Annealing temperature /℃: 760 ~ 800
Hardness after annealing ≤HBW: 240
Quenching temperature /℃: 1050 ~ 1100
Cooling medium: oil
Cooling medium: oil
Common tempering temperature /℃: 600~680
Hardening value after tempering at temperature /MPa |400℃: -
Hardening value after tempering at temperature /MPa |400℃: -
Hardening value after tempering at temperature /MPa |500℃: 1690
Hardening value after tempering at temperature /MPa |600℃: 1670
Hardening value after tempering at temperature /MPa |650℃: 1520
Hardening value after tempering at temperature /MPa |650℃: 1520
AVAILABLE SHAPES
Round bar / flat bar / hollow bar / plate / forgings
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
Round bar / flat bar / hollow bar / plate / forgings
Bright - peeled + polishing, centerless grinding
Forged - ring, tube, pipe casing, discs, shaft
FORMS AND DIMENSIONS AVAILABLE
Round bar (Diameter): 5.5 to 650mm
Steel strip: THK0.15 ~ 2.50 X W5.0 ~ 300mm
Flat bar (Thickness X width): 10 ~ 350 X 15 ~ 620mm
Length: Fixed length or random length or based on the customer's special requirement.
TYPICAL APPLICATIONS
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
TECHNICAL SALES ASSISTANCE & SERVICE
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
Round bar (Diameter): 5.5 to 650mm
Steel strip: THK0.15 ~ 2.50 X W5.0 ~ 300mm
Flat bar (Thickness X width): 10 ~ 350 X 15 ~ 620mm
Length: Fixed length or random length or based on the customer's special requirement.
TYPICAL APPLICATIONS
Cutting tools
Mechanical parts
Air hammer tools
Piercing tools
TECHNICAL SALES ASSISTANCE & SERVICE
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：1.2567 / 30WCrV17-2
Previous page：30WCrV17-2
Last page：X30WCrV9-3